PROBLEM TO BE SOLVED: To provide polypropylene resin composition having superior rigidity, heat resistance, transparency and impact resistance and attaining high productivity, and a medical instrument formed of the polypropylene resin composition.;SOLUTION: The polypropylene resin is composed of a propylene homopolymer having (i) a melt flow rate (ASTM D 1238, 230C, 2.16 kg load) of 10-60 g/10 minutes, (ii) a meso pentad fraction (mmmm) of 0.920-0.950, and (iii) a molecular weight distribution (Mw/Mn) of 2.0-5.6, and not subjected to molecular weight reducing adjustment by a peroxide. This medical syringe is obtained by injection-molding the polypropylene resin, and this prefilled syringe preparation is obtained by filling the medical syringe with a medical solution with a pH of 5.0-9.0.;COPYRIGHT: (C)2008,JPO&INPIT
展开▼
机译:解决的问题:提供具有优异的刚性,耐热性,透明性和耐冲击性并获得高生产率的聚丙烯树脂组合物,以及由该聚丙烯树脂组合物形成的医疗器械。;解决方案:聚丙烯树脂由具有以下特征的丙烯均聚物组成: (i)熔体流动速率(ASTM D 1238,230C,2.16 kg载荷)为10-60 g / 10分钟,(ii)中观五单元组分(mmmm)为0.920-0.950,和(iii)分子量分布(Mw / Mn)为2.0-5.6,并且未通过过氧化物进行分子量降低调节。该医用注射器是通过将聚丙烯树脂注塑成型而获得的,而这种预装注射器的制备是通过向医用注射器中注入pH值为5.0-9.0的医用溶液而获得的。版权所有:(C)2008,JPO&INPIT
展开▼