Nylon and teflon scribe effect on NBR to Chemlok 233 and NBR to NBR bond interfaces

摘要

A study was requested by Manufacturing Engineering to determine what effects marking with nylon (6/6) and Teflon scribes may have on subsequent bonding. Witness panel bond specimens were fabricated by the development lab to test both acrylonitrile butadiene rubber (NBR) to Chemlok and NBR to NBR after controlled exposure. The nylon rod used as a scribe tool demonstrates virtually no bond deterioration when used to scribe lines on either the Chemlok to NBR surfaces or the NBR to NBR interface. Lab test results indicate that the nylon rod-exposed samples produce tensile and peel values very similar to the control samples and the Teflon exposed samples produce tensile and peel values much lower than the control samples. Visual observation of the failure surfaces of the tested samples shows that Teflon scribing produces an obvious contamination to the surface and the nylon produces no effect. Photographs of test samples are provided. It is concluded that Teflon stock used as a scribe tool on a Chemlok 233 to NBR surface or an NBR to NBR surface has a detrimental effect on the bond integrity on either of these bond interfaces. Therefore, it is recommended that the nylon rod continue to be used where a scribe line is required in the redesigned solid rocket motor segment insulation layup operations. The use of Teflon scribes should not be considered.