Performance of high plutonium-containing glasses for the immobilization of surplus fissile materials

摘要

Plutonium from dismantled weapons is being evaluated for geological disposal. While a final waste form has not been chosen, borosilicate glass will be one of the waste forms to be evaluated. The reactivity of the reference blend glass containing the standard amount of Pu ((approximately)0.01 wt %) to be produced by the Defense Waste Processing Facility (DWPF) is compared to that of glasses made from the same nominal frit composition but doped with 2 and 7 wt % Pu, and also equal mole percentages of Gd(sub 2)O(sub 3). The Gd is added to act as a neutron poison to address criticality concerns. The four different glasses have been reacted using the PCT-B method with a SA/V of 20,000 m(sup (minus)1) and the Argonne Vapor Hydration Test (VHT) method. Both test methods accelerate the reaction of the glass. PCT-B is used to determine the reactivity of the glass by analyzing the solution and reacted test components, while the VHT is used to evaluate the long-term reactivity of the glass and the distribution of Pu to secondary phases that will control the long-term reaction of the glass. The results of the tests with high levels of Pu are compared to those with the nominal levels to be produced in the standard DWPF glass.