Gradient Heating Epitaxial Growth Gives Well Lattice-Matched Mo2C-Mo2N Heterointerfaces that Boost Both Electrocatalytic Hydrogen Evolution and Water Vapor Splitting

摘要

An optimized approach to producing lattice-matched heterointerfaces for electrocatalytic hydrogen evolution has not yet been reported. Herein, we present the synthesis of lattice-matched Mo2C-Mo2N hetero-structures using a gradient heating epitaxial growth method. The well lattice-matched heterointerface of Mo2C-Mo2N generates near-zero hydrogen-adsorption free energy and facilitates water dissociation in acid and alkaline media. The lattice-matched Mo2C-Mo2N heter-ostructures have low overpotentials of 73 mV and 80 mV at 10 mA cm~(-2) in acid and alkaline solutions, respectively, comparable to commercial Pt/C. A novel photothermal-electrocatalytic water vapor splitting device using the lattice-matched Mo2C-Mo2N heterostruc-ture as a hydrogen evolution electrocatalyst displays a competitive cell voltage for electrocatalytic water splitting.