Effect of lanthanum on the piezoelectric properties of lead zirconate titanate-lead zinc niobate ceramics

摘要

The effect of lanthanum (La) addition on the piezoelectric properties of lead zirconate titanate-lead zinc niobate (PZT-PZN) was investigated. When small amounts of La were added to the 0.82PZT-0.18PZN, the phase of the specimen changed from rhombohedral to tetragonal and the grain size was steadily reduced. To retain the morphotropic phase boundary (MPB) condition of the specimens with La contents of up to 4 mol%, the Zr/Ti ratio in the PZT was increased to 54/46. When more than 5 mol% La was added, pyrochlore phases were formed, and the piezoelectric properties were reduced. Therefore, the optimum piezoelectric properties (d_(33) = 545 pC/N, k_p = 0.64, and s_(33) = 0.39% at 2 kV/mm) were observed in the specimen having MPB composition and with an La content of 4 mol%.