Composition and structure of coatings based on rare-earth zirconates

摘要

Coatings based on lanthanum, neodymium, samarium, and gadolinium zirconates have been grown by atmospheric plasma spraying of powders, and their composition and structure have been investigated by scanning electron microscopy, chemical analysis, and X-ray diffraction. The results demonstrate that the chemical composition of the coatings differs from the compositions of the powders they were prepared from. During plasma spraying of Ln(2)Zr(2)O(7)-based powders, the rare-earth oxide vaporizes more rapidly than zirconia. The difference in composition between the powders and coatings decreases as the atomic number of the rare earths increases in going from La to Gd. We have studied the processes that take place in the coatings during heat treatment at a temperature of 1250A degrees C. It has been shown that the major phase in the La2Zr2O7-, Nd2Zr2O7-, and Sm2Zr2O7-based coatings undergoes a defect fluorite-pyrochlore structural phase transition. The La2Zr2O7-based coatings have been found to contain similar to 5 wt % t-ZrO2 in addition to the major phase. The Gd2Zr2O7-based coating retained a defect fluorite structure.