Hybrid effect of carbon nanotube and nano-clay on physico-mechanical properties of cement mortar

摘要

In this work, several nanomaterials have been used in cementitious matrices: multi wall carbon nano-tubes (MWCNTs) and nano-clays. The physico-mechanical behavior of these nanomaterials and ordinary Portland cement (OPC) was studied. The nano-clay used in this investigation was nano-kaolin. The metakaolin was prepared by thermal activation of nano-kaolin clay at 750 ℃ for 2 h. The organic ammonium chloride was used to aid in the exfoliation of the clay platelets. The blended cement used in this investigation consists of ordinary Portland cement, carbon nanotubes and exfoliated nano metakaolin. The OPC was substituted by 6 wt.% of cement by nano metakaolin (NMK) and the carbon nanotube was added by ratios of 0.005, 0.02, 0.05 and 0.1 wt.% of cement. The blended cement: sand ratio used in this investigation was 1:2 wt.%. The blended cement mortar was prepared using water/binder ratio of 0.5 wt.% of cement. The fresh mortar pastes were first cured at 100% relative humidity for 24 h and then cured in water for 28 days. Compressive strength, phase composition and microstructure of blended cement were investigated. The results showed that, the replacement of OPC by 6 wt.% NMK increases the compressive strength of blended mortar by 18% compared to control mix and the combination of 6 wt.% NMK and 0.02 wt.% CNTs increased the compressive strength by 29% than control.