Effects of 650℃ aging for 1—1000 h on structure and hydrogen embrittlement susceptibility（HES）of steel Cr21Ni6Mn9N have been investigated.The results show that M23C6 typecarbide precipitates at grain boundaries and Cr-depletive region appears beside them duringaging.The precipitates grow and connect each other as the aging time prolongs.Meanwhile,the degree of Cr-depletion aggravates first and then recovers gradually while the aging time isvery long,i.e.,1000 h.The HES of the steel increases with increasing aging time but does notreduce with the recovery of Cr content at the Cr-depletive region.That implies that the ex-isting of carbides at grain boundaries might be the main reason which promotes the HES ofsteel during aging.