Polyacryonitrile ( PAN) nanofibers were prepared by electrospinning, and amidoximepolyacryonitrile ( AOPAN) nanofibrous membranes were generated by chemical modification of PAN nanofibers, which were used as the filtration membrane for separation of colistin fermentation broth.According to the experimental data, characters materials and comparing nanofibrous membranes filtration separation performance, double-layer nanofibrousmembrane was selected.The optimum operating parameters had been determined:pressure was 0.14 Mpa.Under these optimum parameters, the flux of the nanofibrous membrane was 2.61 L/m2 .min, the protein reta-tion ratio was is nearly 90%, and the part of pigment and other impurities had been removed.%使用静电纺丝再经胺肟化改性制备AOPAN纳米纤维膜,并基于AOPAN纳米纤维膜构建膜分离装置,用于粘杆菌素发酵液的后处理。研究中,对不同厚度的纳米纤维膜的渗透通量及分离性能进行比较,最终确定双层叠合的纳米纤维膜为分离膜,最适操作压力为0.14 MPa。在此条件下,分离膜的渗透通量为2.61 L/m2.min,蛋白质的截留率达到90%,色素等其他杂质也得到有效去除。