A PILOT-PLANT SCALE TEST OF COAL-BASED ROTARY KILN DIRECT REDUCTION OF LATERITE ORE FOR Fe-Ni PRODUCTION

摘要

Nickel pig iron (NPI), used as a substitute for electrolytic nickel, is able to reduce the production cost of stainless steel greatly. Aiming for preparing NPI from nickeliferous laterite ore, a pilot-plant scale test of coal-based rotary kiln direct reduction of laterite ore was performed and reported in this study. In this process, the ground laterite sample (18.85% TFe and 1.52% Ni) mixed with additives, pulverized coal and binder was briquetted into briquettes with the size of 40mm×40mm×31mm, laterite ore briquettes and reducing coal were charged into a rotary kiln with the diameter of 1.6 m and the length of 16 m, for a retention period of 6～7 hours, in which reduction section temperature was ranging from 950～1050 °C. The reduced briquettes were water quenched, ball mill ground and beneficated via low intensity magnetic separation. A magnetic concentrate, Ferronickel powder, with 86.9% TFe and 8.0% Ni was obtained, and the corresponding magnetic recovery of iron and nickel are 75% and 96.3%, respectively.